ThreeBond 2082C Room-temperature-curing, two-part epoxy resin with high shearing adhesive strength

ThreeBond 2082C is a two-part epoxy resin that cures at room temperature (25°C). It has been made less brittle by distributing rubber particles in the resin; therefore it always provides stability and strong bonding. Its working time at room temperature is up to 70 minutes, and it reaches about 90% of its ultimate strength within 24 hours.

·	Provides strong bonding: over 25MPa (250kgf/cm²).
·	Offers prolonged working time and excellent workability.
·	Develops strength quickly, and reaches its ultimate strength within 24 hours at room temperature (25°C).
·	Is easy to blend, because the agents can be measured by eye.

Suitable for bonding a variety of materials, including metals and plastics.

·	Repair of land and water vehicles
·	Bonding of electric and electronic parts
·	Bonding of precision equipment and craftwork
·	Bonding of sporting goods such as skis and rackets

Test items	Units	Main agent	Curing agent	Test method
Color and appearance	-	White	Brown clear	3TS-201-02
Viscosity (25°C)	Pa s(P)	15(150)	16(160)	3TS-210-02
Specific gravity (25°C)	-	1.19	0.98	3TS-213-02
Composition ratio	-	100	100	Capacity ratio
Working time	Min	70		25°C, 100g
Standard curing condition	24 hr at 25°C or 1 hr at 60°C
Hardness	-	D76		3TS-215-01
Peel-shearing adhesive strength	MPa (kgf/cm²)	25 (250): 25°C x 7 days 26 (260): 60°C x 1 hour 28 (280): 80°C x 1hour		3TS-301-11 (Fe-Fe: SPCC)
Peel-shearing adhesive strength	MPa (kgf/cm²)	13 (130): 25°C x 7 days 20 (208): 25°C x 7 days 21 (215): 25°C x 7 days		(Al-Al) (SUS-SUS) (Glass epoxy-glass epoxy)
Peeling adhesive strength	kN/m (kgf/25mm)	2.0 (5.0): 25°C x 7 days 1.7 (4.3): 60°C x 1 hour 1.8 (4.5): 80°C x 1 hour		3TS-304-21 (Fe-Fe: SPCC)

* The values presented are those observed in our tests, and are neither guarantees nor standards. The values given in ( ) are for reference.